Hot Dip Galvanizing
Jump to navigation
Jump to search
About
- Kettles - copper causes premature kettle failure.
- Kettle manufacturer - [1]
- Materials engineered for use in galvanizing operations - the specific property required is
- Wikipedia - [2]
- Zinc Ammonium Chloride - used as flux - [3]. Zaclon in Ohio makes it. [4]
Howto
- Sand blast
- Base bath - 10 minutes min
- Base bath - 7 minutes min
- Flux - ammonium
- Actual dip - 3.5 minutes (until base metal reaches melt temp of 835F)
- Water - trapped water explodes, and is dangerous, so first dip is dangerous and venting must be assured.
- Zinc - 2400 lb blocks are the feedstock for hot dip baths. This is only 0.1 cubic meter - or 4 cubic feet.
https://www.aisc.org/globalassets/modern-steel/archives/2014/08/2014v08_galvanizing.pdf
More about surface preparation: [5]
Sourcing
- Acid -
- Base - KOH pr NaOH for grease - [6], NaOH doesn't require hot water.
- Ammonium chloride - $2/lb [7]
Zinc Ingots
See Zinc#Sourcing
- [8]
- Carter Alloys, 2" zinc balls [9]
- ACI - [10]
- Ney - [11]
- Industrial Metal Supply - [12]. Do they have ingot?
- Victory - [13]
- Milward - [14]
- Umicore - [15]
- Belmont Brooklyn - [16]
- AEM says zinc - [17]
- Ingots on Thomas Register - [18]
- Zinc Ingot on Thomas Register - [19]
- Zinc on Thomas Register - [20]