Polylactic acid/Research Development
Literature review
L (+) lactic acid fermentation and its product polymerization by Narayanan et al reviews the production of lactic acid and its use as a plastic monomer. The synthetic route of lactic acid is four steps that involve fixating an activator cyanide group to an acetylaldehyde to form lactonitrile, hydrolysis of lactonitrile with sulfuric acid to yield lactic acid and ammonium salt. For purification via reactive distillation lactic acid is esterified with methanol to methyl lactate and water, methyl lactate is distilled, and hydrolyzed to lactic acid with the addition of water. The production of lactic acid from biological sources is through the fermentation of high energy carbohydrates to lactic acid by Lactic Acid Bacteria. Lactic acid is neutralized and precipitated with calcium hydroxide. Calcium lactate is collected and hydrolyzed with water. For purification lactic acid is esterified with methanol to methyl lactate and removed via distillation, before hydrolysis with water. Has use as hardener for cellophane.
"The choice of an organism primarily depends on the carbohydrate to be fermented. Lactobacillus delbreuckii subspecies delbreuckii are able to ferment sucrose. Lactobacillus delbreuckii subspecies bulgaricus is able to use lactose. Lactobacillus helveticus is able to use both lactose and galactose. Lactobacillus amylophylus and Lactobacillus amylovirus are able to ferment starch. Lactobacillus lactis can ferment glucose, sucrose and galactose. Lactobacillus pentosus have been used to ferment sulfite waste liquor." Lactobacillus also have complex nutrition requirements. Rhizopus oryzae are also stereoselective LAB as well as yeasts such as Saccharomyces cerevisiae and Kluyveromyces lactis and have been investigated for their usefulness. Lactase enzymes are stereospecfic and heterolactic species have two isoforms, some species induce their second enzyme only under high concentrations of lactic acid. Genetic engineering on lactobacilli has shown success in controlling stereospecficity of products, reaction rate and yield; Rhizopus oryzae is also under study. Favorable feedstocks are high sugar or starch plants. Techniques to increase yield include pretreatments, simultaneous saccharification, and nutrient supplementation (especially nitrogen - yeast extract). Methods to remove lactic acid product from the fermentation batch include ion-exchange resins and electrodialysis.
Different bioreactor configurations have been studied and batch-wise and continuous reactor sketches are provide. Continuous cell recycle reactors have shown high performance and utilize membranes to retain cells while removing media. Cell immobilization by biofilm establishment shows higher performance to free floating culture systems. High cell concentrations make it much more difficult to maintain optimal conditions in all parts of the reactor and can stress the cells (stereoisomerization). "(a) lowering down of the pH of fermented broth (3.0 to 4.2); (b) Use of hydrophilic membrane and the volatile amine weak base (VAWB) to separate lactic acid from the fermented broth through the hydrophillic membrane to VAWB; (c) Regeneration of lactic acid from salts of weak amine base by selectively vaporizing the volatile amine base. This process can be repeated to ensure the efficient separation of free lactic acid and its salt. "
Synthesis of polylactic acid by direct polycondensation under vacuum without catalysts, solvents and initiators by Achmad et al details a procedure. The authors recommend PLA be pursued using processing plants capable of fermenting feedstock, purifying lactic acid, and condensing the product as is proposed for the OSE product ecology. Streptococcus bovis is a LAB suggested for use but the species is also linked to pathogenicity. The process used by the researchers used three phases for treating the lactic acid and polymerizing its monomer: distillation, oligomerization, and polymerization. The reaction was carried out in 4 l sealable flasks, on magnetic stirrers and heaters, with temperature and pressure probes, and connected to a pressure regulator. During distillation sample temperature is brought to 150 C over 90 minutes and maintained for 60 minutes and PLA concentration increases from 90% to 100% as measured by acid-base titrations. Oligomerization phase was a reduction in pressure to 10 mmHg and temperature was raised to 200 C. The polymerization step was maintenance of the reduced pressure and temperature for 89 hours. The condensate was also separated with gel filtration chromatography and measured with a RI detector. Fourier Transform Infrared Spectroscopy was used to analyze molecules functional groups.
[http://144.206.159.178/FT/862/34857/596552.pdf Melt/solid polycondensation of l-lactic acid: an alternative route to poly(l-lactic acid) with high molecular weight] by Moon et al (2000) describes a method that yields high weight PLA on the order of 500,000 daltons through a condensation reaction using a tin chloride dihydrate/p-toluenesulfonic acid binary system. They report that reaction temperatures below the Tm (melting point) of PLA yields a better product and is referred to as melt/solid polycondensation. oligo(l-lactic acid) (OLLA) is mixed with tin(II) chloride dihydrate (SnCl2) (0.4 wt% relative to OLLA) and p-toluenesulfonic acid (TSA) (an equimolar ratio to SnCl2). The mixture is heated to 180 C and the pressure reduced to 10 torres over the period of an hour followed by maintenance for 5 hrs. The product consisting of 20,000 dalton polymers is ground and heated to 105 C under vacuum for 1-2 hr to crystallize the polymers. Solid-state post-polycondensation was initiated by increasing the temperature to 150 C and reducing the pressure to 0.5 Torr. Treatment was continued over 30 hours but molecular weight peaked between 2-10 hours and drastically reduced after 20 hours. The results showed a method to obtain high molecular weight PLLA with comparable characteristics to the lactide ROP synthesis. The method used here catalyzes the first step of dehydration to form lactide and the lactide ROP step follows. The high activity of the catalyst and the ability to move through the amorphous PLLA may be driving the reaction by concentrating ester tails and catalyst in the amorphous regions during crystallization.
(Poly)lactic acid: plasticization and properties of biodegrable multiphase systems by Averous (2001) experimented with measuring the properties of PLA prepared with different plasticizers. Plasticizers included: glycerol, polyethylene glycol, citrate ester, PEG monolaurate, and oligomeric lactic acid. various mixtures of PLA with thermoactive starch polymers (TSP) were prepared and tested. Plasticizer treated samples show a decrease in Tg (glass transition temp) and therefore Tm (melting temp). Oligomeric lactic acid followed by low molecular weight polyethylene glycol were effective plasticizers while glycerol was ineffective. Finding effective methods to combine PLA and TSP would enhance the product.